I-LaSeal 973 yokwelapha ngokushesha iHybrid MS Polymer Sealant
Izinjongo eziyinhloko
1.Ukuvala iminyango namafasitela;
2.Interior usebenzisa
Izici
Isicelo
1.Izixhumanisi zokuxhuma ekwakhiweni kwensimbi yeshidi, ukuvala amasistimu okushisa umoya.
2.I-Elastic bonding ezakhiweni ezidlidlizayo
I-3.Ukuvalwa kwamalunga aphansi kanye nokuhlangana kodonga oluphansi lokunyakaza
4.Ukuvala amalunga ezitsheni, amathangi, izisele njll.
Ishidi Ledatha Yezobuchwepheshe(TDS)
Idatha yobuchwepheshe:Le datha elandelayo ingeyezithenjwa kuphela, ayihloselwe ukusetshenziswa ekulungiseleleni imininingwane
I-LaSeal 973 yokwelapha ngokushesha iHybrid MS Polymer Sealant
Okujwayelekile:
Ihlangabezana noma yeqa izimfuneko zezicaciso ezilandelayo:
Izidingo zokucaciswa kokuqukethwe kwe-VOC kukhredithi ye-LEED EQc4.1
"Imikhiqizo ekhipha kancane" yomthetho we-SCAQMD 1168.
Izidingo ze-VOC yesiFulentshi zekilasi A+
I-CE imakwe i-EN 15651 yezicelo ze-facade.
Into |
Idatha |
Chemical Base |
I-MS Polymer Based |
I-Curing Mechanism |
Ukwelapha Umswakama |
Umbala |
Mhlophe/Mnyama/Mpunga |
Ukuminyana |
1.52 gr/ml |
Thatha Isikhathi Esikhululekile ≤ 1h |
10-20 min (23°C no-%50 RH) |
Isikhathi somsebenzi wokwakha |
10 imiz |
Ukujula okuphulukisiwe (amahora angama-24) |
>3.5mm |
Amandla Okuqina |
≥1.8MPa |
Ukwandisa ngesikhathi sekhefu |
≥200% |
I-100% Tensile Modulus |
≥1.0MPa |
Shore A Ukuqina |
40 - 50 |
Ukumelana ne-UV |
Alukho ushintsho. |
Cindezela Isilinganiso |
>350ml/min |
Shirkage |
≤ 1.5% |
Izinga Lokushisa Lesevisi |
+5°C kuya +35°C |
Izinga Lokushisa Lokusebenza |
-50 ℃ ~ 120 ℃ |
Impilo yeshelufu |
Izinyanga ezingu-12 |
Isimo sokuphulukisa sesampula :23℃×50%RH×14 izinsuku |
Ukulinganiselwa
Akumele isetshenziswe ezindaweni ezivaleleke ngokuphelele lapho okokufaka uphawu kungeke kwelaphe ngenxa yokushoda komswakamo osemkhathini.
I-Multi-Seal ingasetshenziswa ezinhlobonhlobo zama-substrates ngokuqondile. Uma ungaqiniseki, sincoma ukuhlolwa kokuqala kokuhambisana.
Ukulungiswa kwendawo
● Kunconywa ukulandela inqubo yokuhlanza nezinto zokwakha:
● I-Glass Degrease ngotshwala noma i-MEK
● I-Aluminium, ama-alloys alula nensimbi engagqwali Nciphisa ngotshwala noma i-MEK
● Ezinye Izinsimbi I-Lightly abrade bese i-degrease njengenhla
● Ukhuni oluguguleka kancane bese lususa uthuli
● I-Plastics Degrease usebenzisa i-ejenti etuswe umkhiqizi wepulasitiki
● Ukhonkolo nezinye izinto ezine-alkali Hlasha bese ususa uthuli
Isiyalezo
7.Amaphakheji avuliwe kufanele adliwe ngokushesha ngangokunokwenzeka.
8.Izindawo ezingcolile namathuluzi asetshenzisiwe kufanele ahlanzwe ngomoya omhlophe noma ngotshwala. Ihlanzwa ngomshini kuphela ngemva kokwelashwa.
9.Isilinganiso sobubanzi/ubunzulu obuhlangene kufanele sibe ngu-2:1.
Isitoreji nempilo yeshelufu
Ishidi Ledatha Yezobuchwepheshe(TDS)
Idatha yobuchwepheshe:Le datha elandelayo ingeyezithenjwa kuphela, ayihloselwe ukusetshenziswa ekulungiseleleni imininingwane
I-LaSeal 731 Ikhwalithi Ephakathi I-Acetoxy Silicone Sealant
Into |
Idatha |
Uhlobo |
I-acetoxy |
Ukuminyana (g/cm3) |
0.98 |
Ukunyakaza kwamandla |
30% |
isikhathi sokulala |
5-15 imizuzu |
Isikhathi sokumisa (2mm/h) |
8-10 |
Ukomisa(4mm/h) |
18-22 |
Ubukhulu. Amandla aqinile |
1.3 |
Hardness shore A |
21 isiqephu 2 |
I-Elongation at Break(%) |
=500 |
I-Modulus Mpa(100%) |
0.60 |
Izinga lokushisa lohlelo lokusebenza |
-20 C kuya ku +40 C |
Ukumelana nezinga lokushisa |
-50 C kuya +100 C |
Okunamathelayo |
KULUNGILE |
ukumelana nesimo sezulu |
KULUNGILE |
Ingcina ebandayo eshisayo |
KULUNGILE |
ngaphansi kwamanzi okunamathelayo |
KULUNGILE |
Ukubuyiselwa Kwe-Elastical (%) |
96 |
Isilinganiso Sokulahlekelwa Okuningi (%) |
35 |
Imikhawulo: Umkhiqizo awusebenzi ekuhlanganiseni kwesakhiwo noma kuphrojekthi okuyisisekelo sayo sinezinga lokushisa elingaphezulu kuka-40 ℃.